Whistatt offers exceptionally stable and uniform chemical and physical conductivity. When used as an anti-static or resistance agent, the material allows for flexible electrical system design.
These compounds provide the same superior sliding and microscopic reinforcement as our Poticon series, with the added benefit of conductivity or anti-static properties. The three dimensional net-like structure of Whistatt's conductive bypass delivers extremely stable and uniform conductivity.
These compounds provide the same superior sliding and microscopic reinforcement as our Poticon series, with the added benefit of conductivity or anti-static properties. The three dimensional net-like structure of Whistatt’s conductive bypass delivers extremely stable and uniform conductivity.
Polymer
|
PPS
|
PPS
|
PC
|
Special PA
|
PP
|
||
---|---|---|---|---|---|---|---|
Grade
|
RFKB-9
|
RBA313N
|
CB221HC
|
NB362N
|
PW36
|
||
Unit
|
Test method
|
||||||
Water absorption rate
|
%
|
D570
|
0.02 | 0.02 | - | 0.1 | 0.11 |
Tensile strength
|
MPa
|
D638
|
50 | 49 | 67 | 108 | 29 |
Elongation at break
|
%
|
D638
|
1.2 | 1.6 | 5.2 | 2 | 5 |
Flexural strength
|
MPa
|
D790
|
68 | 69 | 103 | 162 | 44 |
Flexural modulus
|
GPa
|
D790
|
5.1 | 5.4 | 3.4 | 10.3 | 2.5 |
Izod impact strength
|
J/m (notched)
|
D256
|
30 | 25 | 27 | 29 | 42 |
Coefficient of kinetic friction
|
*Otsuka method
|
0.22 | 0.18 | - | 0.15 | - | |
Specific abrasion volume
|
X10-1mm3/N・km
|
0.021 | 0.01 | - | 0.02 | - | |
Specific abrasion of counterpart
|
X10-1mm3/N・km
|
0 | 0 | - | 0 | - | |
Heat distortion temperature
|
℃
|
D648
|
213 | 220 | 131 | 200 | 77 |
Flammability
|
UL94
|
V-0 | V-0 | - | HB | - | |
Volume resistivity rate
|
Ωm
|
D257
|
104 | 102 | 1.9×106 | 102 | 109 |
*Otsuka method : This Size is measured size of 90×50×3 mm molded item by vernier caliper